Importance of ion bombardment during coverage of Au nanoparticles on their structural features and optical response

This work studies the changes in the optical response and morphological features of 6 ± 1 nm diameter Au nanoparticles (NPs) when covered by a layer of a-Al2O3 by pulsed laser deposition (PLD). The laser fluence used for ablating the Al2O3 target is varied in order to modify the kinetic energy (KE) of the species bombarding the NPs during their coverage. When the ion KE < 200 eV, the structural features and optical properties of the NPs are close to those of uncovered ones. Otherwise, a shift to the blue and a strong damping of the surface plasmon resonance is observed as fluence is increased. There are two processes responsible for these changes, both related to aluminum ions arriving to the substrate during the coverage process, i.e., sputtering of the metal and implantation of aluminum species in the metal. Both processes have been simulated using standard models for ion bombardment, the calculated effective implanted depths allow explaining the observed changes in the optical response, and the use of a size-dependent sputtering coefficient for the Au NPs predicts the experimental sputtering fractions. In spite of the work is based on PLD, the concepts investigated and conclusions can straightforwardly be extrapolated to other physical vapor deposition techniques or processes involving ion bombardment of metal NPs by ions having KE > 200 eV