Significance of reheat cracks to the integrity of pressure vessels for light-water reactors

Reheat cracks usually manifest themselves as macroscopic defects, which are centimeters long and deep, and are detectable by the usual nondestructive examination (NDE) procedures or as microscopic grain boundary decohesions (GBD) that are beyond the limit of detection by commercial NDE procedures. This report has concentrated on the significance of the microscopic cracks that may go undetected. The probability that GBD exist in the heat-affected zones (HAZ) of weldments of pressure vessel steels is high; particularly in SA 508 Class 2 weldments. A sample of the HAZ from the prolongation-weldment from the Heavy Section Steel Technology program Intermediate Test Vessel (ITV) No. 4 was examined by the Staatliche Materialprufungsanstalt (MPA). They reported GBD 5 mm (0.2 in.) long. This prompted an examination of the HAZ from the ITV vessel that had been tested to failure at 240C (750F). During testing, the region of the weld which contained the flaw that initiated the failure was strained up to 0.5%. A metallographic examination of this region of the weldment revealed GBD, but none of the size reported by the MPA. Further, there was no evidence that the GBD had extended as a consequence of the tests. Fracture toughness tests were made of the HAZ of welds from ITV-4. The electron-beam welding procedure, which permits more accurate siting of the crack, was used. Fracture toughness values in excess of 220 MPa root m (200 ksi root in.) were obtained at -180C