Polyamide 6/nickel ferrite composites: morphological and structural evaluation

This study aims to evaluate the influence of particle size of the load on the structure and morphology of polyamide composite 6/ferrita nickel. To obtain the composite, the polyamide 6 was previously vacuum dried at 80 ° C/48h to eliminate moisture, and then the load was incorporated as powders and as synthesized after calcination at 900°C in the mass concentration of 50%. Subsequently, the mixture was compressed using three tons to obtain the composites, which were characterized by XRD and SEM. XRD results showed the characteristic peaks of polyamide 6 and ferrite. An increase in crystallinity was observed for the composite loaded calcined at 900° C. SEM results showed a good dispersion of nickel ferrite loading in the matrix, the presence of larger clusters and evenly distributed load for the composite calcined at 900 ° C. (author)