Remaining life assessment of carbon steel boiler headers by repeated creep testing

The condition of carbon steel boiler headers that have been in service for over 25 years has been assessed periodically by NDT, dimensional measurements, replication and accelerated creep testing. Historical temperature records were limited, so estimates of effective header temperatures were made from replicas. These estimates were compared with header stub thermocouple readings. At about 280,000 service hours, samples were chain-drilled from the headers for accelerated creep testing. These test results indicated that the headers had satisfactory remaining life. Nine years after the original samples were taken, additional samples were removed from one header at 337,000 service hours. The creep rupture properties measured from the repeated tests were almost identical to the initial results. A mild degree of random, nodular graphite was found in the samples and its effect on creep properties is discussed