Comparison of results analysis of chemical composition of alloys inside the U-Zr-Nb by XRF and AAS techniques

U-Zr-Nb alloy chemical composition analysis using X Ray Fluorescence (XRF) and Atomic Absorption Spectroscopy (AAS) techniques have been conducted, where U-Zr- Nb alloy was chosen as candidates for new high-density fuel for future research reactors . Composition analysis is necessary because the composition of elements in the fuel will determine the characteristics of fuel during the fabrication process and in the reactor. The use of two kinds of analysis techniques were designed to obtain accurate analysis results. The experiment was conducted to determine the major element composition and impurities in the alloy U-Zr-Nb. First U-Zr-Nb varying alloy composition Nb were respectively 1%, 4%, 7% (U10% Zr1% Nb, U10% Zr4% Nb and U10% 7% Nb) as results of the melting process of measuring the diameter of 120 mm crushed on the surface bottom. Once on the bottom surface is smooth, then analyzed using XRF techniques. To analyze the elements using AAS techniques, alloy U-Zr-Nb cut into 10 mm x 5 mm then dissolved using HF and nitric acid. Solution that occurred were analyzed using AAS technique. From the analysis using the XRF technique is obtained the alloy U-10% Zr-1% Nb, U-10% Zr-4% Nb and Zr-10% U-7% Nb) had a content of each element as follows: U (87.8858%), Zr (2.6097%) and Nb (0.2206%), U (87.8556%), Zr (2.6302%), and Nb (0.6573%); U (84.6334%), Zr (2.5773%), and Nb (1.0940) weight. Results of analysis using AAS techniques on samples obtained third consecutive Zr content of 9.25%, 8.90% and 9.80% while the content of Nb was not detected. Meanwhile, the results of elemental analysis of impurities in all three samples showed that almost all the elements are still qualify as fuel except Zn element. Element Zn at the three samples of each alloys U-10% Zr-1% Nb, U-10% Zr-4% Nb and U-10% Zr-7%Nb is 1.3266%, 3.2756% and 1.0927% weight. It could be concluded that the results of analysis of elemental content and impurities in the alloy U-Nb-Zr using both XRF and AAS visible that results of the analysis technique which is was approach composition of U-Zr-Nb alloy that planned by using AAS technique. (author)