The yield drop at or below 423 K in Zr single crystals and in Ti

Yield drops were obtained in interrupted tensile and compression tests performed on zirconium single crystals between 262 and 362 K. Near 295 K, where most tests were performed, a minimum yield drop was obtained for an aging performed near the internal stress. For positive stress relaxations and a constant aging time, this yield drop increased linearly with the stress relaxed during aging. This result indicates a significant portion of the yield drop is caused by dislocations gliding to pinning points, which are most probably forest dislocations. A similar behaviour was observed for polycrystalline titanium at 423 K. The yield drops observed in the single crystals at 295 K, after aging at zero stress, increased linearly with the logarithm of the aging time in contrast to the time-independent Haasen-Kelly effect observed in polycrystalline material. (auth)