Particularities of hydride phase segregation in zone of channel tube destruction and slow hydride cracking mechanisms

Creators

  • 1. Moskovskij Inzhenerno-Fizicheskij Institut, Moskva (Russian Federation)
  • 2. Korejskij Issledovatel'skij Institut Atomnoj Ehnergii, Tedzhon (Korea, Republic of)

Description

Destruction surface of hydrogenated channel tube samples which were prepared from Zr-2,5%Ni alloy on CANDU technology and annealed for stress removal was studied. X-ray reflexions from hydride precipitates at the destruction surface and hydride phase texture were observed

Additional details

Additional titles

Original title (Russian)
Особенности выделения гибридной фазы в зоне разрушения канальных труб из сплава Зр-2,5% Нб и механизмы замедленного гибридного растрескивания

Publishing Information

Journal Title
Voprosy Atomnoj Nauki i Tekhniki. Fizika Radiatsionnykh Povrezhdenij i Radiatsionnoe Materialovedenie
Journal Issue
no.2
Journal Page Range
p. 58-70
ISSN
0134-5400
CODEN
VAFMDP

INIS

Country of Publication
Ukraine
Country of Input or Organization
Ukraine
INIS RN
33009784
Subject category
S36: MATERIALS SCIENCE;
Descriptors DEI
ANNEALING; CRACK PROPAGATION; FRACTURE MECHANICS; FRACTURE PROPERTIES; HYDRIDES; HYDROGEN EMBRITTLEMENT; NIOBIUM ADDITIONS; PHYSICAL RADIATION EFFECTS; REACTOR CHANNELS; X RADIATION; ZIRCONIUM BASE ALLOYS
Descriptors DEC
ALLOYS; ELECTROMAGNETIC RADIATION; EMBRITTLEMENT; HEAT TREATMENTS; HYDROGEN COMPOUNDS; IONIZING RADIATIONS; MECHANICAL PROPERTIES; MECHANICS; NIOBIUM ALLOYS; RADIATION EFFECTS; RADIATIONS; REACTOR COMPONENTS; TRANSITION ELEMENT ALLOYS; ZIRCONIUM ALLOYS