Effects of oxygen and hydrogen at low pressure on the mechanical properties of V-Cr-Ti alloys

Exposure of V-Cr-Ti alloys to low oxygen partial pressures at high temperature results in oxygen absorption and internal oxidation. Characterization of a V-4Cr-4Ti alloy after oxidation at 500 deg. C revealed a microstructure with ultrafine oxide precipitates in the matrix and along grain boundaries. Heat treatment at 950 deg. C following oxidation resulted in large TiOx precipitates in the matrix and grain boundaries. Tensile ductility was reduced by exposure to low-pressure oxygen under the temperature and pressure conditions. However, heat treatment at 950 deg. C following oxidation was generally effective in recovering ductility irrespective of initial annealing treatment or grain size. Without increases in oxygen, >500 wppm hydrogen was required to cause significant decreases in tensile elongation. When oxygen was added either during or prior to hydrogen exposure, significant embrittlement occurred with 100 wppm hydrogen. Because of this synergism with hydrogen, oxygen pick-up remains a major concern for V-Cr-Ti alloys in fusion reactor applications