Platinum boride nanowires: Synthesis and characterization

Highlights: ► Platinum boride nanowires have been synthesized via the direct current arc discharge method. ► XRD, TEM and SAED indicate that the nanowires are single-crystal PtB. ► Two broad photoluminescence emission peaks at about 586 nm and 626 nm have been observed in the PL spectroscopy of PtB nanowires. - Abstract: Platinum boride (PtB) nanowires have been successfully fabricated with direct current arc discharge method using a milled mixture of platinum (Pt) and boron nitride (BN) powders. X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were used to characterize the compositions, morphology, and structures of the samples. The results show that PtB nanowires are 30–50 nm thick and 20–30 μm long. TEM and selected area electron diffraction (SAED) patterns identify that the PtB nanowires are single-crystalline in nature. A growth mechanism based on vapor–liquid–solid (VLS) process is proposed for the formation of nanowires.