Analysis of the characteristics of a white organic LED using the newly synthesized blue material methyl-DPVT by varying the thickness of the DPVBi layer

A two-wavelength type of white organic light-emitting diode (OLED) having a blue/orange emitting layer was fabricated by synthesizing Methyl-DPVT, a new derivative of the blue-emitting material DPVBi on the market. The white-emission of the two-wavelength type was successfully obtained by representing not only blue emission by using DPVBi but also orange emission by using methyl-DPVT as a host material and Rubrene as a guest material. The basic structure of the fabricated white OLED is glass/ITO/NPB(150 A)/DPVBi/methyl-DPVT :Rubrene [2.0 wt%](100 A)/BCP(70 A)/Alq3(150 A)/Al(600 A). To evaluate the characteristics of the devices, we varied the thickness of the DPVBi layer from 100 A to 80 A to 60 A. A nearly pure white-emission was obtained in CIE coordinates of (0.3327, 0.3397) when the DPVBi layer was 60-A thick at an applied voltage of 11 V. The device started to operate at 1 V and to emit light at 2.5 V. The external quantum efficiency was above 0.5 % both when almost all of the current was injected and the applied voltage was over 10 V. A superior maximum quantum effciency of 0.746 % was obtained at an applied voltage of 18.5 V.