Life prediction of repaired welds in a pressurised CrMoV pipe with incorporation of initial damage

Creep damage FE modelling was performed for fully and partially repaired, thick-walled, circumferential pipe weldments, in which initial damage was incorporated into the calculations to take account of the material degradation of the aged materials. The pipe welds were subjected to a realistic internal pressure and axial loading, the latter of which is allowed to vary within the range allowed by design codes. The material properties used are related to a CrMoV weldment at 640 deg. C. The initial damage distribution was numerically determined using an established procedure. A full post weld heat treatment is assumed to be carried out and the effects of welding induced residual stresses were neglected. The results obtained cover a number of initial damage levels, magnitudes of axial load, and repair excavation depth. On this basis, the sensitivities of the failure life of the repaired welds to these important factors can be evaluated. It was found that both the peak initial damage and the total life are very sensitive to the repair time, particularly when system load is high. The effect of the repair depth for depth: thickness ratios ≥0.5 is generally small for these loadings. There could be a significant benefit if the initial damage in the HAZ of the repair weld, which could be relatively high when the repair time is relatively large, could be reduced by repair welding or by post weld heat treatment