Microstructural evaluation of Ti-35Nb-7,5 T alloy deformed by cold rolling and annealed

This work presents the main results of microstructural characterization of Ti- 35Nb-7.5Ta (% in weight) deformed by cold rolling and annealed. Samples were obtained by electric arc melting, heat treated at 1000 deg C for 8 hours and water quenched. Samples were deformed by cold rolling in multiple passes up to a maximum reduction of 84%. Deformed samples were encapsulated in quartz under vacuum and annealed at 600, 700 e 800 deg C, in variable times and water quenched. Characterization was carried out using light optical microscopy, X-ray diffraction, Vickers hardness test and acoustic emission measurements to determine the Young's modulus. The results show the orientation occurrence of the martensitic phase in relation to the cold rolling direction in deformed samples. In samples annealed at 600 deg C recovery is predominant and samples annealed at 800 deg C for 60 min are fully recrystallized. (author)