Microstructure and crystallographic texture evolution during TIG welding of zircaloy-2 material

Zirconium and its alloys are extensively used as structural materials in nuclear reactors, because of better neutron economy, good corrosion resistance in water and good mechanical properties at operating temperature. Zircaloy-2 and zircaloy-4 are widely used in both pressurized water reactors (PWR) and boiling water reactors (BWR) as fuel cladding materials and as calandria tube and pressure tube materials in pressurized heavy water reactors (PHWR). The satisfactory performance and the life of the reactor components depend mainly upon their mechanical properties, corrosion properties and dimensional stability in the reactor condition, which are strong function of metallurgical parameters such as microstructure and texture. Therefore, for best performance of the reactor components these parameters are optimized during their fabrication. The microstructure and texture of the zircaloy-2 components are expected to get modified during the welding of the components. In this study the evolution of the microstructure and texture has been investigated as a function of the welding parameters. Heat input was varied the current and welding time. A variety of analytical techniques have been applied for the study on microstructure and texture of the welds. Optical microscopy and electron microscopy were used to evaluate the detailed microstructure. X-ray diffraction (XRD) was used investigate the crystallographic textures among the base metal, heat affected zone and fusion zone. Particular attention was focused on the determination of microtexture in weld by using electron backscatter diffraction (EBSD) technique. After that, an effort was put to compare the results of X-ray macro-texture and EBS-microtexture. (author)