Stress corrosion cracking of nickel base alloys characterization and prediction

For many years, studies have been carried out in several laboratories to characterize the IGSCC (Intergranular Stress Corrosion Cracking) behaviour of nickel base alloys in aqueous environments. For their relative shortness, CERTs (Constant Extension Rate Tests) have been extensively used, especially at the Corrosion Department of the CEA. However, up to recently, the results obtained with this method remained qualitative. This paper presents a first approach to a quantitative interpretation of CERT results. The basic datum used is the crack trace depth distribution determined on a specimen section at the end of a CERT. It is shown that this information can be used for the calculation of initiation and growth parameters which quantitatively characterize IGSCC phenomenon. Moreover, the rationale proposed should lead to the determination of intrinsic cracking parameters, and so, to in-service behaviour prediction