Non-isothermal crystallization kinetics of Fe₂O₃–CaO–SiO₂ glass containing nucleation agent P₂O₅/TiO₂

Fe₂O₃–CaO–SiO₂ glass ceramics containing nucleation agent P₂O₅/TiO₂ were prepared by sol-gel method. The samples were characterized by X-ray diffraction (XRD) and differential scanning calorimetry (DSC). The activation energy and kinetic parameters for crystallization of the samples were calculated by the Johnson-Mehi-Avrami (JMA) model and Augis-Bennett method according to the results of DSC. The results showed that the crystallization mechanism of Fe₂O₃–CaO–SiO₂ glass, whose non-isothermal kinetic parameter n = 2.3, was consistent with surface crystallization of the JMA model. The kinetics model function of Fe₂O₃–CaO–SiO₂ glass, f(α) = 2.3(1–α)[–ln(1–α)]^0.57, was also obtained. The addition of nucleation agent P₂O₅/TiO₂ could reduce the activation energy, which made the crystal growth modes change from onedimensional to three-dimensional.