Fracture toughness determination of the pressure vessel steel A508 Cl 2 between 100 and 350 degree C

The fracture toughness of the pressure vessel steel A508 was determined in the temperature range 100 - 350 degree C. The J-integral method with crack growth resistance curves, the so-called R-curves, was used. The results show that the steel does not have an 'upper-shelf' and the fracture toughness, K sub (JC), decreases with increasing temperature to a minimum around 300 degree C and an increase above it. These results are compared to those obtained previously on an other pressure vessel steel A533B which has essentially the same temperature dependence. The results were also analysed using the Tearing modulus, T. The conclusion iw that the crack growth resistance and the crack initiation resistance (K sub (JC)) show a significant decrease around the operating temperatures as compared to 100 degree C. (author)