Boron effect on plasticity of austenite chromium-nickel-manganese steel with nitrogen

Plasticity of the stainless steels, with boron content changing from 0 to 0.13% is investigated. It follows from the test results that when the boron content amounts to 0.001 - 0.005%, plasticity of the steel rises at temperatures from 800 to 1000 deg C. When the boron content is higher, plasticity of the steel drops down, particularly at a temperature of 1000 deg C. Due to high sensitivity of the test steel to overheating at temperatures above 1260 deg C, the temperatures of 1240 -1260 deg C are considered to be the optimum for ingot heating, provided that the ingots are preliminarily held at the first stage of heating at a temperature of 1200 - 1220 deg C