The Characteristics of Welding Joint on Stainless Steel as a Candidate of High Level Waste Canister

High level waste is the waste generated from reprocessing of the spent fuels. This type of waste is vitrified with borosilicate glass to become waste-glass. This waste glass is contained in a canister made of austenitic stainless steel. The canister material is subjected to be welded during fabrication and utilization. The character of the welding joint that is the function of the electrical current used in the welding process have been studied. The strength of the joint is tested mechanically i.e.: the tensile strength and hardness test. The result shows that the higher the current used in welding process, the better the strength of the joint and as well the tensile strength. The optimum current is 110 A. From the hardness test, it was figured that the length of the HAZ area is 14 mm. The material in HAZ area is the hardest compared to the others, it is due to the appearance of the chrome-carbide. The welding of the canister with such a condition, during fabrication as well as during the utilization of the canister for the container of the high level waste with the PWHT process gives better result. (author)