Evaluation of polymer-coated CsI:Tl as an alpha/beta pulse shape discriminating flow-cell

A pulse shape discriminating flow-cell radiation detection system constructed with polymer coated CsI:Tl was evaluated for simultaneous gross alpha/gross beta quantification. The CsI:TI scintillator was crushed and sieved to 63-90 μm particle size and microencapsulated with Parylene C to reduce its rate of dissolution. Averaged over the first hour of use, the pulse shape discrimination figure-of-merit was 1.4 and the detection efficiencies were 64.9 ± 5.7 %, 52.5 ± 4.5 % and 4.5 ± 0.2 % for 233U, 90Sr/90Y and 14C , respectively. The typical background count rate in the alpha and beta pulse shape window was 0.17 and 0.004 cps, respectively. The resultant minimum detectable activity for a 30 second count time was calculated to be 0.19 ± 0.01 Bq, 0.9 ± 0.1 Bq and 11.4 ± 0.6 Bq for 233U, 90Sr/90Y and 14C, respectively. Although the 3 μm thick microencapsulation reduced CsI:Tl dissolution, the detection efficiency declined by a factor of two after 4.8 hours while the pulse shape resolution degraded slightly