Effect of twice quenching and tempering on the mechanical properties and microstructures of SCRAM steel for fusion application

The effect of twice quenching and tempering on the mechanical properties and microstructures of SCRAM steel was investigated. The results from tensile tests showed that whether twice quenching and tempering processes(1253 K/0.5 h/W.C(water cool) + 1033 K/2 h/A.C(air cool) + 1233 K/0.5 h/W.C + 1033 K/2 h/A.C named after 2Q and 2TI, and 1253 K/0.5 h/W.C + 1033 K/2 h/A.C + 1233 K/0.5 h/W.C + 1013 K/2 h/A.C named after 2Q and 2TII)increased strength of steel or not depended largely on the second tempering temperature compared to quenching and tempering process(1253 K/0.5 h/W.C + 1033 K/2 h/A.C named after 1Q and 1T). Charpy V-notch impact tests indicated that twice quenching and tempering processes reduced the ductile brittle transition temperature (DBTT). Microstructure inspection revealed that the prior austenitic grain size and martensite lath width were refined after twice quenching and tempering treatments. Precipitate growth was inhibited by a slight decrease of the second tempering temperature from 1033 to 1013 K. The finer average size of precipitates is considered to be the main possible reason for the higher strength and lower DBTT of 2Q and 2TII compared with 2Q and 2TI.