Laboratory results of stress corrosion cracking of steam generator tubes in a complex environment - An update

Stress corrosion cracking occurs in the flow-restricted areas on the secondary side of steam generator tubes of Pressured Water Reactors (PWR), where water pollutants are likely to concentrate. Chemical analyses carried out during the shutdowns gave some insight into the chemical composition of these areas, which has evolved during these last years (i.e. less sodium as pollutants). It has been modeled in laboratory by tests in two different typical environments: the sodium hydroxide and the sulfate environments. These models satisfactorily describe the secondary side corrosion of steam generator tubes for old plant units. Furthermore, a third typical environment - the complex environment - which corresponds to an All Volatile Treatment (AVT) environment containing alumina, silica, phosphate and acetic acid has been recently studied. This particular environment satisfactorily reproduces the composition of the deposits observed on the surface of the steam generator tubes as well as the degradation of the tubes. A review of the recent laboratory results obtained by considering the complex environment are presented here. Several tests have been carried out in order to study initiation and propagation of secondary side corrosion cracking for some selected materials in such an environment. 600 Thermally Treated (TT) alloy reveals to be less sensitive to secondary side corrosion cracking than 600 Mill Annealed (MA) alloy. Finally, the influence of some related factors like stress, temperature and environmental factors are discussed. (authors)