Formation of Gd-Al alloy films by a molten salt electrochemical process

The electrochemistry of molten LiCl-KCl-GdCl3 at a reactive Al electrode has been studied at 723 to 823 K. Electrochemical techniques such as cyclic voltammetry and chronopotentiometry have been used in order to identify the intermetallic compounds formed. Cyclic voltammetry showed that, while at an inert W electrode GdCl3 is reduced to Gd metal in a single step at a potential close to the reduction of the solvent, at an Al electrode a shift towards more positive values occurs. This shift of the cathodic potential indicated a reduction of the activity of Gd in Al with respect to that of W, due to the formation of alloys. The surface characterization of samples formed by both galvanostatic and potentiostatic electrolysis has shown the presence of two intermetallic compounds: GdAl3 and GdAl2. Using open-circuit chronopotentiometry it has been possible to measure the potentials at which these compounds are transformed into each other. The values of these potential plateaus, once transformed into e. f. m. values, allowed to determine the thermodynamic properties of the GdAl3 intermetallic compound. (orig.)