Reversible martensitic ω-α transformation in Ti and Zr

The mechanism of phase transformation in pure Ti and Zr in samples with initial ω-structure, produced as a result of heating to 1400 K with subsequent increase in pressure up to 8 GPa and a sharp decrease in temperature and pressure to normal values, has been studies. As a result of α → β → ω transformation, occurring in the process of the above-mentioned treatment, grains of ω-phase with perfect rystal structure are formed. With ω-phase heating to 650 K formation of α-phase takes place, and it is accompanied by the appearance of characteristic martensitic relief on the sample surface. Subsequent application of high pressure results in the reverse α → ω transformation with the disappearance of surface relief.The data suggest that direct ω → α transformation while heating and reverse α → ω transformation under pressure are realized according to martensitic mechanism