Effects of the Substitution of the Mo Element W of Super Duplex Stainless Steel Weld on the Secondary Phase Formation and Corrosion Resistance

To investigate the effect of tungsten substitution of molybdenum on the formation of the second phase in Super Duplex Stainless Steel Weldments, welding wires with a composition of 3 wt% Mo, 2.2 wt% Mo-2.2 wt% W were designed for the flux cored arc welding process. As a result, the precipitation of the χ phase and σ phase increased in proportion to the decrease in the amount of δ ferrite content because the reaction, δ ferrite → σ + γ2, proceeded as the temperature rose. Under the same experimental conditions, the precipitation of the second phase, which degrades the properties of the material, was significantly reduced in the W substitution specimens compared to the Mo-only specimens. A polarization test conducted in a salt solution revealed that the pitting potential of the W substitution specimens was higher than that of the Mo-only specimens.