Radiation induced defects in natural diamond and their annealing

Creators

  • 1. Troitskij Inst. Innovatsionnykh i Termoyadernykh Issledovanij (TRINITI), Troitsk (Russian Federation)

Description

The coefficients of equations for increase and decrease in the lines of seven defects of the 2a-type diamond are obtained on the basis of the data on the analysis of the spectra in the visible area for different times of annealing at 550 deg C. Formation of the defects by the neutron irradiation and their transformation by the vacuum annealing in the samples of the 2a-type natural diamond constituting a wide-zone photo-semiconductor with a low nitrogen content, are studied. For transformation of the defects created in the diamond sample after irradiation in a nuclear reactor it was isothermally annealed at 550 deg C during several tens of hours periodical removal from the vacuum furnace within the interval of ten hours

Abstract (Russian)

На основе данных анализа спектров в видимой области для разных времен отжига при 550 град. С получены коэффициенты уравнений роста и спада линий семи дефектов алмаза типа IIa. Исследовались образование при нейтронном облучении и трансформация при вакуумном отжиге дефектов в образцах природного алмаза типа IIa, являющегося широкозонным фотополупроводником с небольшим содержанием азота. Для трансформации дефектов, созданных в алмазном образце после облучения в ядерном реакторе, его изотермически отжигали при 550 град. С в течение нескольких десятков часов с периодическим извлечением из вакуумной печи с интервалом в десять часов

Additional details

Additional titles

Original title (Russian)
Радиационно-наведенные дефекты в природном алмазе и их отжиг

Publishing Information

Journal Title
Pis'ma v Zhurnal Tekhnicheskoj Fiziki
Journal Volume
26
Journal Issue
11
Journal Page Range
p. 36-40
ISSN
0320-0116
CODEN
PZTFDD

INIS

Country of Publication
Russian Federation
Country of Input or Organization
Russian Federation
INIS RN
33016997
Subject category
S75: CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND SUPERFLUIDITY;
Descriptors DEI
ABSORPTION SPECTRA; ANNEALING; CRYSTAL DEFECTS; DIAMONDS; NEUTRONS; PHYSICAL RADIATION EFFECTS; SPECTRA UNFOLDING; TIME DEPENDENCE
Descriptors DEC
BARYONS; CARBON; CRYSTAL STRUCTURE; DATA PROCESSING; ELEMENTARY PARTICLES; ELEMENTS; FERMIONS; HADRONS; HEAT TREATMENTS; MINERALS; NONMETALS; NUCLEONS; PROCESSING; RADIATION EFFECTS; SPECTRA

Optional Information

Notes
8 refs., 2 figs.