Evaluation of long-term relaxation for high-strength bolted connections

It is general that the clamping forces of high-strength bolts diminish within a certain time period after the initial clamping force. In case that special treatments are applied on a faying surface, the clamping force is relaxed severely. Tests were conducted for slip critical joints subjected to various faying surface parameters. The candidates for bolt were two kinds: Korean Standard and American Standard. Relaxation occurred for slip resistant joints with an uncoated surface that had been shot-blasted, cleaned, milled or rusted. In case of ASTM hexagon bolts, the initial clamping force dropped from 7.9% to 13.6% after 1, 000 hours while relaxation ratio was the range from 8.7% to 15.4% for KS bolts. For ASTM hexagon bolt joints with a 5 mil thick zinc coating, the clamping force of the bolts decreased 15.0%, while relaxation ratio was 12.85% for KS bolts. For 4.9 mil thick red lead painted treatment, the relaxation ratio was 18.7% for ASTM hexagon bolt, 34.9% for KS bolts. Regardless of faying surface treatments, the first week charged at least 86% of total relaxation from this test. (authors)