Carbon formation under thermo-catalytic pyrolysis of hydrocarbons

Process of catalytic thermo-cracking directed on generation of carbon-containing compositions is considered. Filling of carbon for clays and mixture of clay with the Turgaj slurry in 1:1 ratio has been conducted during 30 min within temperature range 450-900 deg C on running pyrolysis facility under propane-butane mixture flow rate 70-75 mm3/min. Study of the structure change and the samples content was conducted by IR- and EPR-spectroscopy method. It was determined that samples filling of carbon is carrying out by carbide mechanism. New materials which can operate in capacity of sorbents for sewage waters purification from ions of heavy metals and organic substances are received