Synthesis and characterization of ceramic membranes for micro filtration

This paper presents the results of a preliminary research work in the development of ceramic membranes by moulding process. The two major objectives were to determine the effect of operating parameters ori- the membrane sheet and membrane characterization. The starting material for the membrane was powdered aluminum oxide and alumina granules. Alumina granules were obtained by spray drying of mixture of alumina with additives and binders under specific conditions. The membrane sheet was produced by mould pressing at various pressures and then sintering at different temperatures. Membrane characterization was done based on microstructure using SEM, pore size distribution, density, and porosity. Strong and porous membranes were produced at pressing force of 120 -140 kN and sintering temperature of 1400 -1500 'C. Pore size and porosity obtained was in the range of 2 -10 μ m, and 13 - 48% respectively. These membranes can be used for, microfiltration at elevated temperature and under extreme environmental condition. They can also be used as porous support for the production qf composite asymmetric UF/hyperfiltration, and gas separation membranes. Further work in the refinement of' pore-size and permeation studies is envisaged