Crystallization kinetics of isotactic polypropylene nucleated with octamethylenedicarboxylic dibenzoylhydrazide under isothermal and non-isothermal conditions

Octamethylenedicarboxylic dibenzoylhydrazide (TMC-300) was used as a nucleating agent for isotactic polypropylene (iPP) for the first time. The Avrami method and the Caze method were used to analyze the isothermal and non-isothermal crystallization kinetics of iPP incorporated with TMC-300, respectively. During isothermal crystallization, the half crystallization time at 130 °C reduces from 130 s of virgin iPP to 44 s after addition of TMC-300, which reflects that TMC-300 increased the crystallization rate of iPP obviously. The crystallization activation energy decreases from 382.5 kJ mol⁻¹ of virgin iPP to 275.3 kJ mol⁻¹ of iPP/TMC-300. During non-isothermal crystallization, the crystallization peak temperature of iPP nucleated with TMC-300 was increased by 5.1 °C when compared to that of virgin iPP at the cooling rate of 20 °C min⁻¹, and both the reduction of half crystallization time and the increase in peak crystallization temperature also justified that the addition of TMC-300 accelerated the crystallization of iPP.