Dislocations and related defects in niobium oxide structures

Lattice images of the niobium oxides, structures based on the linkage of octahedral groups in continuous networks, occasionally contain features recognizable as dislocations. Since lattice imaging enables the microstructure to be resolved in greater detail, at the level of local structural organization, it is possible to determine the configuration, and also to infer the chemical composition, of dislocated areas. By treating the niobium oxide 'block' structures as superstructures of the ReO3 (DO9) type, the topology of dislocations can be expressed by relations between the insertion (or deletion) of one or more half-planes of cations, or of oxygen atoms only, changes in the number of crystallographic shear plane interfaces between blocks or columns, changes in (idealized) dimensions and any requisite distortion in the third dimension. Mapping the structure around a dislocation, from the lattice image, is directly equivalent to plotting the Burgers' circuit. In this way, the precise nature of a dislocating perturbation and its implications for the local chemical composition of the crystal can be directly identified. The method is exemplified by analysis of dislocations and of related extended defects of several types, associated with twinning phenomena, semicoherent intergrowth between different ReO3-type superstructures and arrays building up a low angle boundary. The essential features of the analysis are not restricted to structures of the niobium oxide type, but can be extended to other types of polyhedron networks. (author)