Effect of substrate properties on morphology of nanosized films of BaxSr1-xTiO3
- 1. RAN, Fiziko-Tekhnicheskij Inst. im. A.F. Ioffe, Sankt-Peterburg (Russian Federation)
- 2. Sankt-Peterburgskij Gosudarstvennyj Ehlektrotekhnicheskij Univ. (LEhTI), Sankt-Peterburg (Russian Federation)
Description
Initial stages of BaxSr1-xTiO3 films growth on diverse dielectric substrates were studied by the method of intermediate-energy ions scattering. On the basis of the results obtained microdefects in the film were analyzed. It was detected that, depending on the shape, size and electrostatic state of crystallographic cells on the substrate surface, the character of film growth varies. Epitaxial growth occurs on SrTiO3 substrate. Film on LaAlO3 substrate consists of slightly misoriented crystallites. Film growth on MgO sublayer has an insular character up to 20 nm thickness and formation of foreign phases takes place; increase in the film thickness gives rise to epitaxial character of growth. A polycrystal film containing textured units is grown on the surface of α-Al2O3 (1102)
Abstract (Russian)
Начальные стадии роста пленок BaxSr1-xTiO3 на различных диэлектрических подложках исследованы методом расссеяния ионов средних энергий. На основании полученных результатов проведен анализ микродефектов в пленке. Обнаружено, что в зависимости от формы, размеров и электростатического состояния кристаллографических ячеек поверхности подложки меняется характер роста пленки. На подложке SrTiO3 происходит эпитаксиальный рост. Пленка на подложке LaAlO3 состоит из слегка разориентированных кристаллитов. Характер роста пленки на подложке MgO островковый до толщины 20 нм, при этом происходит образование посторонних фаз; при увеличении толщины пленка приобретает эпитаксиальный характер роста. На поверхности α-Al2O3 (1102) растет поликристаллическая пленка, содержащая текстурированные блокиAdditional details
Additional titles
- Original title (Russian)
- Влияние свойств подложек на морфологию нанометровых пленок Ба
Publishing Information
- Journal Title
- Fizika Tverdogo Tela
- Journal Volume
- 45
- Journal Issue
- 6
- Journal Page Range
- p. 1070-1075
- ISSN
- 0367-3294
- CODEN
- FTVTAC
INIS
- Country of Publication
- Russian Federation
- Country of Input or Organization
- Russian Federation
- INIS RN
- 35081307
- Subject category
- S36: MATERIALS SCIENCE;
- Descriptors DEI
- ALUMINIUM OXIDES; BARIUM COMPOUNDS; CRYSTAL GROWTH; DEFECTS; GRAIN ORIENTATION; INTERFACES; MAGNESIUM OXIDES; SOLID SOLUTIONS; STRONTIUM TITANATES; SUBSTRATES; THICKNESS; THIN FILMS
- Descriptors DEC
- ALKALINE EARTH METAL COMPOUNDS; ALUMINIUM COMPOUNDS; CHALCOGENIDES; DIMENSIONS; DISPERSIONS; FILMS; HOMOGENEOUS MIXTURES; MAGNESIUM COMPOUNDS; MICROSTRUCTURE; MIXTURES; ORIENTATION; OXIDES; OXYGEN COMPOUNDS; SOLUTIONS; STRONTIUM COMPOUNDS; TITANATES; TITANIUM COMPOUNDS; TRANSITION ELEMENT COMPOUNDS
Optional Information
- Notes
- 12 refs., 2 figs., 1 tab.