Efficiency of tantalum electroplate in the presence of strong depassivator
Creators
- 1. KNTs RAN, Inst. Khimii i Tekhnologii Redkikh Ehlementov i Mineral'nogo Syr'ya, Apatity (Russian Federation)
Description
It is determined, whether the thin electrolytic coating, applied to the item from the much cheaper material, retains the unique properties of the voluminous tantalum. The studied samples constitute the plates from the St3 or Cr18N10T steel, covered with the ∼50 μm tantalum layer. It is shown, that the tantalum coating, electrodeposited from the melt, reliably protects the steel not only from the acid corrosion, but also from the local anode depassivation by the chloride in the acid solutions at least up to 80 Deg C
Abstract (Russian)
Определяли, сохраняет ли тонкое электролитическое танталовое порытие, нанесенное на изделие из более дешевого материала, уникальные свойства объемного тантала. Изучаемые образцы представляли собой пластины из стали Ст3 или Х18Н10Т, покрытые ∼50 мкм слоем тантала. Показано, что танталовое покрытие, электролитически осажденное из расплава, надежно защищает сталь не только от кислотной коррозии, но и от локальной анодной депассивации хлоридом в растворах кислот по меньшей мере до 80 град СAdditional details
Additional titles
- Original title (Russian)
- Эффективность электроосажденного танталового покрытия в присутствии сильного депассиватора
Publishing Information
- Journal Title
- Zashchita Metallov
- Journal Volume
- 38
- Journal Issue
- 4
- Journal Page Range
- p. 407-411
- ISSN
- 0044-1856
- CODEN
- ZAMEA9
INIS
- Country of Publication
- Russian Federation
- Country of Input or Organization
- Russian Federation
- INIS RN
- 35026040
- Subject category
- S36: MATERIALS SCIENCE;
- Descriptors DEI
- CARBON STEELS; CORROSION PROTECTION; ELECTRODEPOSITED COATINGS; ELECTROPLATING; HYDROCHLORIC ACID; STEEL-CR18NI10TI; TANTALUM; TEMPERATURE RANGE 0273-0400 K
- Descriptors DEC
- ALLOYS; AUSTENITIC STEELS; CARBON ADDITIONS; CHLORINE COMPOUNDS; CHROMIUM ALLOYS; CHROMIUM-NICKEL STEELS; COATINGS; CORROSION RESISTANT ALLOYS; DEPOSITION; ELECTRODEPOSITION; ELECTROLYSIS; ELEMENTS; HALOGEN COMPOUNDS; HEAT RESISTANT MATERIALS; HEAT RESISTING ALLOYS; HIGH ALLOY STEELS; HYDROGEN COMPOUNDS; INORGANIC ACIDS; INORGANIC COMPOUNDS; IRON ALLOYS; IRON BASE ALLOYS; LYSIS; MATERIALS; METALS; NICKEL ALLOYS; PLATING; REFRACTORY METALS; STAINLESS STEELS; STEELS; SURFACE COATING; TEMPERATURE RANGE; TITANIUM ADDITIONS; TITANIUM ALLOYS; TRANSITION ELEMENT ALLOYS; TRANSITION ELEMENTS
Optional Information
- Notes
- 7 refs.; 5 figs.; 3 tabs.