On peculiarities of using cathodes on tungsten-rhenium alloy base in vacuum luminescent low-voltage indicators

A comparative study of cathodes prepared from W wire (VAI-AP) and from a W-Re alloy (VAR5) with a cathodoluminophor of ZnO-Zn and carbonate coatings indicates that the initial values of the anode current and the luminophor brightness are almost the same for both cathodes. The stability of the anode current and of the luminescent properties of the luminophor, however, were much better for the VAR5 cathode with a coating of ternary, fine-grained carbonate. This is attributed to the difference in the amount of active material sputtered on the cathode luminophor. The temperature of the alloy cathode is 30-40deg lower than that of the W cathode, which creates favorable conditions for decreasing the sputtering from the cathode. The operational lifetime of the cathode is also increased for this alloy