Effects of impurities on hydrogen permeability through palladium alloy membrane at comparatively high pressure and temperature

Palladium alloy membrane method is considered to be a useful technique for fusion reactor fuel purification process. To study the feasibility of this method, the effects of impurities on permeation characteristics of palladium alloy membrane were examined. Experiments were carried out at practical conditions: pressure; 120 - 1200 kPa, temperature; about 700 K. No poisoning effect on hydrogen permeability of commercial Pd-Ag (Au.Ru) alloy was observed for impurities such as NH3, CH4, CO, CO2, O2 and N2, which were mixed with hyper-pure H2 at low concentration level (10 - 10000 ppm). Deterioration occurred by contamination with oil vapor. However, regeneration of the membrane was easily performed by air baking followed by hydrogen reduction. Chemical reactions in the permeation cell were also examined. (author)