Track profile and range studies of heavy and light ions in CR-39: effect of thermal pre-treatment on etching characteristics

Sheets of CR 39 have been irradiated with 20Ne, 32S, 40Ar, 56Fe and 63Cu ions at normal incidence to the surface of the sheets and at normal incidence to the edges. The profiles of the etched tracks have been observed side-on and measurements made of the variation of V (the ratio of track to bulk etching velocities) along the tracks and of the fully etched range of the tracks. Heating the plastic at 1000C prior to etching produces zones within the plastic having different bulk etching rates Vsub(B). An outer zone of low Vsub(B) is followed by a zone of much higher Vsub(B). This allows tracks to be readily etched to very large diameters, comparable in size to the breakdown spots produced by electrochemical etching. (author)