Angle dependent optical properties of polymer films with a biomimetic anti-reflecting surface replicated from cylindrical and tapered nanoporous alumina

Anodic porous alumina nanostructures have been fabricated with tapered and cylindrical pores with a spacing of 100 and 200 nm and depth of 180–500 nm. The porous nanostructures were replicated into polymer films to create a moth-eye anti-reflecting surface by a roll-to-roll UV replication process. The angle dependent optical transmission of the resulting polymer films exhibited up to a 2% increase in transmission at a normal angle and up to a 5% increase in transmission at a 70° angle of incidence to an equivalent film with a surface replicated from polished aluminum. No significant difference was observed between the optical performance of moth-eye surfaces formed from cylindrical and tapered nano-pores. (paper)