Clarification of chemical state for alloying elements in iron rust using a binary-phase potential-pH diagram and physical analyses

A binary-phase potential-pH diagram has been investigated to evaluate the chemical stability of various kinds of double oxide rusts (Fe-X) to get a principle for alloy design enhancing the corrosion resistance of steels. It was found that there are the following types of alloying elements enhancing the corrosion resistance of steels in the rust: (1) iron substitution type (Ni), (2) oxide formation type (Al), (3) metallic type (Ru), and (4) oxygen-acid salt type (WO4). X-ray photoelectron spectroscopy and transmission electron microscopy analyses have been conducted on the rust formed on the low alloy steel in a saline environment. The analytical results were discussed using potential-pH diagrams. The iron substitution type and the oxide formation type elements make spinel double oxides with iron. In the corrosion tests, steels added with Ni or Al had high corrosion resistance. Thus it is possible to obtain high corrosion resistance by the creation of spinel double oxide such as Fe2NiO4 and FeAl2O4 in an inner layer. On the other hand it was found that the metallic type and the oxygen-acid salt type elements were not contained into the iron rust. In particular the oxygen-acid salt elements were excluded from the iron rust and concentrated into the defects of the rust. It is suggested that insoluble salts like FeWO4 are formed on the base metal in the defects to act as an anodic inhibitor. Thus, the addition of a small quantity of W gives high corrosion resistance. The penetration of Cl ions can be prevented by the spinel double oxide in an inner layer and the oxygen-acid salt in the defects. In this way, the high corrosion resistance by the addition of these elements can be understood from the potential-pH diagram and the physical analyses