The glow curve structure for the LiF:Mg,Cu,Na,Si TL detector with dopants concentrations and sintering temperatures

The glow curve structures for LiF:Mg,Cu,Na,Si TL detectors with various dopant concentrations and sintering temperatures were investigated for the improvement of the glow curve structure and sensitivity of the TL detector. The dopant concentrations were varied over the following ranges: Mg (0-0.25 mol%), Cu (0-0.07 mol%), Na and Si (0-1.5 mol%). With increasing Cu concentration, the intensity of the main peak was intensified and reached a maximum at a concentration of 0.05 mol%. The high-temperature peak was reduced. The dependency of the main peak intensity on the Mg concentration exhibits a sharp maximum at 0.2 mol%. The intensity of the high-temperature peak tends to rise slightly with increasing Mg concentration. It was found that the optimum concentrations of the dopants in the LiF:Mg,Cu,Na,Si TL material are Mg: 0.2 mol%, Cu: 0.05 mol%, Na and Si: 0.9 mol%. The dependency of the main peak intensity on sintering temperature exhibits a very sharp maximum at 830 deg. C. The high-temperature peak was rapidly reduced after 825 deg. C