Effect of pre-deformation temperature on reverse transformation characteristic in Fe-Mn-Si based alloys

Two alloys of A: Fe-28Mn-6Si-5Cr(wt.%) and B: Fe-13Mn-5Si-12Cr-6Ni(wt.%) with different Ms temperatures were selected to be subjected to tensile deformation under different temperatures. The effect of deformation temperature on shape memory effect (SME) and the reverse transformation kinetics were studied respectively. It was found that: (1) The best SME could be obtained by deformation at Ms temperature; (2) The As temperature varied with deformation temperature. The lower the deformation temperature was, the lower the As temperature would be; (3) Some non-transformation related strain recovery between deformation temperature and As temperature was observed to be resulted from the retraction of stacking faults. The facts that the variation of As temperature with deformation temperature, as well as the non-transformation strain recovery imply that the γ→ε martensitic transformation in Fe-Mn-Si based shape memory alloys exhibits quasithermoelastic property. (orig.)