Electroless plating of copper on polyimide films modified by surface-initiated atom-transfer radical polymerization of 4-vinylpyridine

Surface modification of polyimide (PI) films were first carried out by chloromethylation under mild conditions, followed by surface-initiated atom-transfer radical polymerization (ATRP) of 4-vinylpyridine (4VP) from the chloromethylated PI surfaces. The composition and topography of the PI surfaces modified by poly(4-vinylpyridine) (P4VP) were characterized by X-ray photoelectron spectroscopy (XPS) and atomic force microscopy (AFM), respectively. The P4VP brushes with well-preserved pyridine groups on the PI surface was used not only as the chemisorption sites for the palladium complexes without prior sensitization by SnCl2 solution during the electroless plating of copper, but also as an adhesion promotion layer to enhance the adhesion of the electrolessly deposited copper to the PI surfaces. The T-peel adhesion strength of the electrolessly deposited copper on the modified PI surface could reach about 6.6 N/cm. Effects of the polymerization time and the activation time in the PdCl2 solution on the T-peel adhesion strength of the electrolessly deposited copper in the Sn-free process to the modified PI surface were also studied