Structure and properties of the alloying zone formed upon electron-beam weld deposition of the coating from chrome-manganese iron alloyed with nitrogen over low-carbon steel

Creators

  • 1. SO RAN, Inst. Fiziki Prochnosti i Materialovedeniya, Tomsk (Russian Federation)
  • 2. Tomskij Politekhnicheskij Univ., Tomsk (Russian Federation)

Description

Structure, properties and residual stresses are investigated in a fusion zone which is formed on electron-beam building-up of wear resistant coating of chromium-manganese cast iron with a nitrogen alloyed austenitic matrix on thin-walled low carbon steel articles. It is revealed that in the process of building-up a fusion zone 10-12 μm wide and free of carbide precipitations occurs. The zone is characterized by enhanced elastic properties and microhardness as well as minimum residual microstress values

Abstract (Russian)

Изучены структура, свойства и остаточные напряжения в зоне сплавления, формирующейся при электронно-лучевой наплавке износостойкого покрытия из хромомарганцевого чугуна с аустенитной матрицей, легированной азотом, на тонкостенные изделия из низкоуглеродистой стали. Установлено, что в процессе наплавки образуется зона сплавления шириной 10-12 мкм, свободная от выделений карбидных частиц. Зона сплавления характеризуется повышенными упругими свойствами и микротвердостью, а также минимальной величиной остаточных микронапряжений

Additional details

Additional titles

Original title (Russian)
Структура и свойства зоны сплавления, формирующейся при электронно-лучевой наплавке покрытия из чромомарганцевого чугуна, легированного азотом, на низкоуглеродистую сталь

Publishing Information

Journal Title
Metallovedenie i Termicheskaya Obrabotka Metallov
Journal Issue
no.2
Journal Page Range
p. 19-22
ISSN
0026-0819
CODEN
MTOMAX

INIS

Country of Publication
Russian Federation
Country of Input or Organization
Russian Federation
INIS RN
38092404
Subject category
S36: MATERIALS SCIENCE;
Descriptors DEI
CARBON STEELS; CAST IRON; CHEMICAL COMPOSITION; COATINGS; ELECTRON BEAM MELTING; HARD FACING; HEAT AFFECTED ZONE; MICROHARDNESS; MICROSTRUCTURE; NITROGEN ADDITIONS; PHASE STUDIES; RESIDUAL STRESSES; SUBSTRATES; THICKNESS; YOUNG MODULUS
Descriptors DEC
ALLOYS; CARBON ADDITIONS; DIMENSIONS; HARDNESS; IRON ALLOYS; IRON BASE ALLOYS; MECHANICAL PROPERTIES; MELTING; PHASE TRANSFORMATIONS; SILICON ALLOYS; STEELS; STRESSES; TRANSITION ELEMENT ALLOYS; ZONES

Optional Information

Notes
8 refs., 3 figs., 2 tabs.