Analysis of the polymeric film and fine dust obtained in plasma of acetylene and acetylene-nitrogen

The results are presented from the resistance analyses to the corrosion of the polymeric covering obtained in plasma of acetylene, on a substrata of aluminum alloy, with the techniques of metallographic analysis, infrared and electrochemical, as much for the fine dust as for the grown film on aluminum. Also, the results of the electrochemical test of polarization made to these films will be shown, which demonstrated an improvement of 2.6 and 4.6 times in the resistance to the corrosion when the material treaty is exposed NaCl 0.2 N and Na H2 PO4 01 M, respectively, in comparison with the substrata without recovering. For the movie obtained in acetylene /nitrogen plasma on steel 1016 the micrographs of the superficial structure of the material they will be shown before and after being treated, which were used to measure the thickness of the cover; also, it will be given to know the results of the tests of adhesion and qualitative analysis of resistance before diverse chemical agents (such as: Benzene, Toluene, H2SO4, HNO3, NaCl, CACO3 NaOH and KOH) and the resistance results are presented from the cover to them