Relationship between thermal embrittlement and hydrogen cracking in 18Ni(250) maraging steel

The role of grain boundary precipitate structure on the stress corrosion susceptibility of 18Ni(250) maraging steel was examined. Varying solution treatment procedures were used to achieve either a precipitate-free grain boundary or one containing a high density of Ti(C,N) particles. The introduction of these treatments, although drastically affecting the monotonic fracture toughness, did not significantly alter the stress corrosion threshold in 100 percent relative humidity. These results are shown to be consistent with the previous suggestion that, under open circuit conditions, hydrogen-assisted cracking controls the environmental crack growth behavior of 18Ni maraging steels. (U.S.)