Preparation of quaternized dimethylaminoethylmethacrylate grafted nonwoven fabric for the removal of phosphate

Dimethylaminoethylmethacrylate (DMAEMA) grafted polyethylene/polypropylene (PE/PP) nonwoven fabric was prepared by radiation-induced graft polymerization. Grafting conditions were optimized and about 150% DMAEMA grafted samples were used for further experiments. DMAEMA graft chains were later quaternized with dimethyl sulphate for the removal of phosphate ions. Adsorption experiments were conducted with quaternized DMAEMA grafted fabric for phosphate removal at low (0.5-25 ppm) and high phosphate concentrations (50-1000 ppm). Adsorbed phosphate amounts at pH 7 were found to be 63 mg phosphate/g polymer and 512 mg phosphate/g polymer for low (25 ppm) and high phosphate concentrations (1000 ppm) respectively showing the efficiency of the adsorbent material in removing phosphate. The pH effect on phosphate adsorption showed that the quaternized DMAEMA grafted nonwoven fabric can adsorb phosphate over a wide pH range (5.00-9.00) indicating that adsorbent material can effectively remove different forms of phosphate ions, namely H2PO4-, HPO42- and PO43- in aqueous solution at this pH range where the species exist. Competitive adsorption experiments were also carried out with two concentration levels at pH 7 to investigate the effect of competing ions. Phosphate adsorption on quaternized DMAEMA grafted nonwoven fabric was found to be higher than the other competing ions at two concentration levels. At high concentration level, the adsorption order was phosphate>nitrite>bromide>sulphate>nitrate whereas at low concentration level, the order was phosphate≅sulphate>bromide>nitrite>nitrate.