High-pressure phase transitions of LaF3 and CeF3
- 1. RAN, Inst. Fiziki, Vysokikh Davlenij im. L.F. Vereshchagina, Troitsk (Russian Federation)
Description
Lanthanum trifluoride base nonstoichiometric solid solutions, LaF3, CeF3 are taken as examples to discuss the influence of high pressure on tisonite-type structure rearrangement. In system of MF2-LaF3 (M - Pb, Sr) the fluorite-like solid solutions M1-xLaxF2+x in a range of 0.5 ≤ x ≤ 0.75 are obtained by quenching from 1500-1700 K at p = 10 GPa. The extrapolation of concentration dependences of solid solution cubic lattice parameters in the systems given for an undoped LaF3 cell results in a=5.86±0.02 A. With the help of X-ray diffraction method a first-order transition in CeF3 under pressure is detected which is analogous to earlier observed transition in LaF3. At p = 20.6 GPa rhombic lattice parameters constitute a = 8.062 ± 0.006 A, b = 8.457 ± 0.009 A, c = 5.091 ± 0.006 A, a volume decrease on transition - 7.3%
Abstract (Russian)
На примере LaF3, CeF3 и нестехиометрических растворов на основе трифторида лантана обсуждается влияние высокого давления на перестройку структуры типа тисонита. В системах MF2-LaF3 (M - Pb, Sr) закалкой от 1500-1700 К при р = 10 ГПа получены флюоритоподобные твердые растворы M1-xLaxF2+x в интервале 0.5 ≤ x ≤ 0.75. Экстраполяция концентрационных зависимостей параметров кубических элементарных ячеек твердых растворов в указанных системах дает для ячейки чистого LaF3 значение а = 5.86±0.02 A. Методом рентгеновской диффракции под давлением зафиксирован фазовый переход первого рода в CeF3, аналогичный недавно найденному переходу в LaF3. Параметры ромбической элементарной ячейки при р = 20.6 ГПа составляют a = 8.062 ± 0.006 A, b = 8.457 ± 0.009 A, c=5.091 ± 0.006 A, уменьшение объема при переходе - 7.3%Additional details
Additional titles
- Original title (Russian)
- Фазовые переходы в LaF
Publishing Information
- Journal Title
- Neorganicheskie Materialy
- Journal Volume
- 39
- Journal Issue
- 11
- Journal Page Range
- p. 1384-1388
- ISSN
- 0002-337X
- CODEN
- NEOMB8
INIS
- Country of Publication
- Russian Federation
- Country of Input or Organization
- Russian Federation
- INIS RN
- 36100351
- Subject category
- S36: MATERIALS SCIENCE;
- Descriptors DEI
- CERIUM FLUORIDES; LANTHANUM FLUORIDES; LATTICE PARAMETERS; PHASE TRANSFORMATIONS; PRESSURE RANGE GIGA PA; QUENCHING; SOLID SOLUTIONS; STOICHIOMETRY; STRONTIUM FLUORIDES; TEMPERATURE RANGE 1000-4000 K; TRIGONAL LATTICES
- Descriptors DEC
- ALKALINE EARTH METAL COMPOUNDS; CERIUM COMPOUNDS; CRYSTAL LATTICES; CRYSTAL STRUCTURE; DISPERSIONS; FLUORIDES; FLUORINE COMPOUNDS; HALIDES; HALOGEN COMPOUNDS; HOMOGENEOUS MIXTURES; LANTHANUM COMPOUNDS; MIXTURES; PRESSURE RANGE; RARE EARTH COMPOUNDS; SOLUTIONS; STRONTIUM COMPOUNDS; TEMPERATURE RANGE
Optional Information
- Notes
- 21 refs., 4 figs., 1 tab.