Synthesis of Barium Titanate from Titanyl Acylate Precursor by Sol-precipitate Method

Nanometersize barium titanates (BaTiO3:BT) powders can be obtained by sol-precipitate method in the presence of polyoxyethylene (20) sorbiton monooleate (Tween-80) as a polymeric surface modifier in a strong alkaline solution (pH > 13). FT-IR, TG/DTA, SEM and XRD were used to investigate the effects of the surfactant influence on the morphology of the obtained BaTiO3 powders. With adding surfactant, a slower rate of hydrolyzation is observed and the rate of condensation is slower. The addition of Tween-80 surfactant in general leads to the formation of smaller particle size of BaTi)3 (70-100 nm). Without adding surfactant, larger particle size of BaTiO3 (100-200 nm) was obtained. The nanometersize BaTiO3 powders were readily sintered at 1000-1200C. Raman-active modes of tetragonal phase BT were detected from Raman spectra of BaTiO3 between 8000C to 12000C.