Encapsulation of spent nuclear fuel-safety analysis

Two methods of encapsulation are studied, both including a copper canister. In one process the copper canister with the spent fuel is filled with copper powder and pressed to solid copper metal at high pressure. In the other process lead is cast around the fuel before the canister is sealed by electron beam welding. The activity decay of the fuel has been going on for 40 years before it arrives to the encapsulation station. This is the basic reason for expecting less activity release and less contamination of the plant than would be the case with fuel recently taken out from the reactors. In analysing the plant safety, experience from the nuclear power plants, from the planning of the Swedish central storage facility for spent fuel (CLAB) and from La Hague has been used. The analysis is also based on experience of todays technology, although it should be possible to improve the encapsulation process further before time has come to actually build the plant. The environment activity release will be very low, both at normal operation and following accidents in the plant. Using very conservative release rates also the most severe anticipated accident in the plant will induce a dose to critical group of only 3 μSv. The staff dose can also be kept low. Due to remote handling, fuel damage will not primarily give staff dose. Of the totally anticipated staff dose of 150 man mSv/year the greatest portion will come from external radiation during repair work in areas where fuel containing canisters by failure can not be taken away. The hot isostatic pressed (HIP) canister process contains more operations than does the lead casting and welding procedure. It is therefore expected to give the highest activity release and staff dose unless extra measures are taken to keep them low. Using remote operation and adequate equipment the encapsulation station with any of the two processes can be built and run with good radiological safety. (author)