Development and investigation of thermomechanical regimes of deforming the base ingots made of 05Kh18AN10 steel
- 1. OAO 'Izhorskie zavody', (Russian Federation)
Description
In connection with the participation in the international project on building the accelerator in Swiss the technology of manufacturing plates of a difficult to work steel 05Kh18AN10 20-120 mm thick is developed for welded structures. It is established that steel limit plasticity noticeably increases with strain rate and is weakly dependent on chemical element contents with a standard steel composition. It is shown that metal ductility on rolling is higher than on forging. The deoxidation with silicocalclium along with the modification with boron at optimal melting temperature is noted to improve essentially the workability of cast steel
Abstract (Russian)
В связи с участием в международном проекте по строительству ускорителя в Швейцарии разработана технология изготовления листов толщиной 20-120 мм из труднодеформируемой стали 05Х18АН10 для сварных конструкций. Установлено, что предельная пластичность стали заметно возрастает с увеличением скорости деформации и слабо зависит от содержания химических элементов в пределах марочного состава. Показано, что технологическая пластичность металла при прокатке выше, чем при ковке . Отмечено, что раскисление силикокальцием и модифицировние бором при оптимальной температуре плавки существенно улучшает деформируемость литой сталиAdditional details
Additional titles
- Original title (Russian)
- Разработка и исследование термомеханических режимов деформации крупных слитков из стали 05Kh18AN10
Publishing Information
- Journal Title
- Izvestiya Vysshikh Uchebnykh Zavedenij. Chernaya Metallurgiya
- Journal Issue
- no.1
- Journal Page Range
- p. 46-49
- CODEN
- IVUMAX
INIS
- Country of Publication
- Russian Federation
- Country of Input or Organization
- Russian Federation
- INIS RN
- 36060569
- Subject category
- S36: MATERIALS SCIENCE;
- Descriptors DEI
- CHEMICAL COMPOSITION; CHROMIUM-NICKEL STEELS; CRACKS; DUCTILITY; FORGING; HOT WORKING; MELTING; METALLURGICAL EFFECTS; PLATES; REDUCTION; ROLLING; STRAIN RATE; TEMPERATURE DEPENDENCE; TEMPERATURE RANGE 1000-4000 K; THERMOMECHANICAL TREATMENTS; THICKNESS
- Descriptors DEC
- ALLOYS; CARBON ADDITIONS; CHEMICAL REACTIONS; CHROMIUM ALLOYS; DIMENSIONS; FABRICATION; HEAT TREATMENTS; HIGH ALLOY STEELS; IRON ALLOYS; IRON BASE ALLOYS; MATERIALS WORKING; MECHANICAL PROPERTIES; NICKEL ALLOYS; PHASE TRANSFORMATIONS; STAINLESS STEELS; STEELS; TEMPERATURE RANGE; TENSILE PROPERTIES; TRANSITION ELEMENT ALLOYS
Optional Information
- Notes
- 7 figs., 2 tabs.