Photoluminescent behavior of heat-treated porous alumina films formed in malonic acid

In the present work IR spectroscopy, electron probe microanalysis (EPMA) and photoluminescence (PL) spectral measurements were applied to study the effect of treatment temperature (T) on compositional and luminescent properties of malonic acid alumina films. Our studies have shown that the heat treatment of anodic alumina films at investigated temperatures from 100 up to 700 deg. C changes their photoluminescence spectra considerably. An increase in T results in the PL intensity growth. When reaching its maximum at 600 deg. C the luminescence intensity then decreases drastically with further T growth. The films heat-treated at 500 and 600 deg. C demonstrate asymmetrical PL band with Gaussian peaks at 437 and 502 nm. We proved that the malonic acid species incorporated into the alumina bulk during the film formation are responsible for photoluminescence band with its peak at 437 nm.