Discoloration of plasticized PVC upon irradiation

The effects of the factors on the discoloration of PVC cross-linked by electron irradiation, such as irradiation dose, the polymerization degree of PVC resin, plasticizers and stabilizers, were studied. The composition of the plasticized PVC used for the experiment was 100 PHR of PVC, 50 PHR of plasticizer, 5 PHR of stabilizer and 5 PHR of cross-linking agent (TMPMA). Three samples with the different degree of polymerization of the PVC resin were used, namely 750, 1050 and 2600. As the plasticizers, phthalic acid esters (DBP, DOP, DIDP), trimellitic acid esters (TOTM, n-TOTM), fatty acid esters (DOS, DOZ), polyester and epoxy group plasticizers were used. The irradiation dose for the test was 3, 6 and 12 Mrad. The experimental results are summarized as follows. As the electron irradiation dose was higher, the resultant discoloration was more remarkable, and the optimum irradiation dose was below 6 Mrad. The degree of polymerization of the PVC resin did not affect the irradiation discoloration. However it was noticed that the cross-linking efficiency was better as the degree of polymerization was higher. The cross-linking efficiency was better as the content of plasticizer was more. The fatty acid esters and epoxy groups showed less discoloration and better cross-linking efficiency. Tin and barium-zinc stabilizers were good. (Kako, I.)